Takahiro HANDA Mitsuru OHTAKE Masaaki FUTAMOTO
Fe thin films were deposited directly and via Ag underlayer on glass and MgO(100) substrates by MBE. Polycrystal Fe films grew on the glass substrate while single crystal films grew on the MgO(100) substrate. Fe film growth followed the Volmer-Weber mode for both cases. The Fe film structure was influenced by the surface roughness of Ag underlayer at the early stage of film growth. The relationships between the Fe thin film morphology and the magnetic properties are discussed.
Nojima and Fujita have found a universal relation, irrespective of temperatures T, between the reduced field hH/Hir(T) and the reduced quantity of magnetization hysteresis mΔM (T, H)/ΔM (T, H0), where Hir is the irreversibility field and ΔM(T, H) is the hysteresis of magnetization for YBa2Cu3Ox and Bi2Sr2CaCu2Ox films. We could explain this universal relation based on a scaling theory in a three-dimensional superconducting vortex-glass phase. The exponent ν derived by this relation coincides with that obtained by nonlinear I-V characteristics for YBa2Cu3Ox films.