Gold on connector contacts is superior in environmental resistance. However, pores existing gold film are source to trigger the corrosion reaction between gold and base metal. For examination of the contacts, it has been popular to apply "Salt Spray Test" and "Sulfur Dioxide Test. " There are some differences of the corrosion products between two tests. Main metal forming the product in Salt Spray is Copper, and main metal in Sulfur Dioxide is Nickel. To investigate the reason, we tried to employ an electro-chemical method. As a result, it was found that there was the difference between the respective galvanic cell combinations generated through pores.
The copyright of the original papers published on this site belongs to IEICE. Unauthorized use of the original or translated papers is prohibited. See IEICE Provisions on Copyright for details.
Copy
Tadashi SHINTANI, "Corrosion Mechanism Analysis of Salt Spray Test and Sulfur Dioxide Test on Gold Plated Connector Contact" in IEICE TRANSACTIONS on Electronics,
vol. E81-C, no. 3, pp. 356-361, March 1998, doi: .
Abstract: Gold on connector contacts is superior in environmental resistance. However, pores existing gold film are source to trigger the corrosion reaction between gold and base metal. For examination of the contacts, it has been popular to apply "Salt Spray Test" and "Sulfur Dioxide Test. " There are some differences of the corrosion products between two tests. Main metal forming the product in Salt Spray is Copper, and main metal in Sulfur Dioxide is Nickel. To investigate the reason, we tried to employ an electro-chemical method. As a result, it was found that there was the difference between the respective galvanic cell combinations generated through pores.
URL: https://global.ieice.org/en_transactions/electronics/10.1587/e81-c_3_356/_p
Copy
@ARTICLE{e81-c_3_356,
author={Tadashi SHINTANI, },
journal={IEICE TRANSACTIONS on Electronics},
title={Corrosion Mechanism Analysis of Salt Spray Test and Sulfur Dioxide Test on Gold Plated Connector Contact},
year={1998},
volume={E81-C},
number={3},
pages={356-361},
abstract={Gold on connector contacts is superior in environmental resistance. However, pores existing gold film are source to trigger the corrosion reaction between gold and base metal. For examination of the contacts, it has been popular to apply "Salt Spray Test" and "Sulfur Dioxide Test. " There are some differences of the corrosion products between two tests. Main metal forming the product in Salt Spray is Copper, and main metal in Sulfur Dioxide is Nickel. To investigate the reason, we tried to employ an electro-chemical method. As a result, it was found that there was the difference between the respective galvanic cell combinations generated through pores.},
keywords={},
doi={},
ISSN={},
month={March},}
Copy
TY - JOUR
TI - Corrosion Mechanism Analysis of Salt Spray Test and Sulfur Dioxide Test on Gold Plated Connector Contact
T2 - IEICE TRANSACTIONS on Electronics
SP - 356
EP - 361
AU - Tadashi SHINTANI
PY - 1998
DO -
JO - IEICE TRANSACTIONS on Electronics
SN -
VL - E81-C
IS - 3
JA - IEICE TRANSACTIONS on Electronics
Y1 - March 1998
AB - Gold on connector contacts is superior in environmental resistance. However, pores existing gold film are source to trigger the corrosion reaction between gold and base metal. For examination of the contacts, it has been popular to apply "Salt Spray Test" and "Sulfur Dioxide Test. " There are some differences of the corrosion products between two tests. Main metal forming the product in Salt Spray is Copper, and main metal in Sulfur Dioxide is Nickel. To investigate the reason, we tried to employ an electro-chemical method. As a result, it was found that there was the difference between the respective galvanic cell combinations generated through pores.
ER -