Thin (Ba0.75Sr0.25)TiO3 (BST) films to be used as dielectric materials in 256 Mbit DRAM capacitors were investigated. These films were deposited by an rf-sputtering method at substrate temperatures of 480 to 750. As substrate temperature increases, the dielectric constant to the films also increases, from 230 to 550. BST films prepared at temperatures higher than 700 show larger current leaks than films prepared at lower temperatures. A dielectric constant of 250, corresponding to a silicon oxide equivalent thickness (teq) of 0.47 nm, and a leak current density about 110-8 A/cm2 were obtained in 30-nm-thick film deposited at 660. Both of these values are sufficient for use in a 256 Mbit DRAM capacitor.