1-5hit |
Relative-Refractive-Index-Difference (Δ) dependence of intrinsic loss of GeO2-Doped graded index silica fibers is clarified in the practical range of 1Δ2% and λ1.5 µm. It is confirmed that the decisive factor of Δ dependence is ultraviolet absorption loss, and that the Δ dependence of scattering loss is small.
Yoshito SHUTO Hirotsugu SATO Shuichi YANAGI Masayoshi OHNO Shin SUMIDA Shunichi TOHNO
We successfully fabricated split alignment sleeves for single-mode operation with the injection-molding technique using both thermosetting epoxy resin and thermoplastic polyetherimide (PEI) resin. The relationship between the surface smoothness and the connection-loss characteristics of these injection-molded plastic sleeves was investigated. We made two-dimensional contour maps of the outer and inner surfaces of the plastic sleeves using the measured surface roughness. There were many contour lines on both the outer and inner surfaces of the PEI sleeve. In contrast, the epoxy sleeves had very smooth surface profiles. An offset Δr was estimated by using the inner-surface roughness data of the sleeve-ferrule contact regions. The connection loss of the sleeve increased as the Δr value increased. The measured losses agree fairly well with the theoretical losses estimated by using the Δr values. The PEI sleeves exhibited large Δr values, and one-third of them had large connection losses of > 0.5 dB. In contrast, the epoxy sleeves had very small Δr values of < 0.6 µm, and exhibited an average loss of < 0.1 dB.
Yoshito SHUTO Shuichi YANAGI Masayoshi OHNO Hirotsugu SATO Shin SUMIDA Shunichi TOHNO
We examined the creep properties and hazard rates of plastic ferrules to ensure the long-term reliablity of optical fiber connections. The endface deformation ΔL had to be smaller than 3 µm to keep the insertion-loss and return-loss fluctuation to acceptable levels in the worst case of random concatenation of similarly deformed plastic ferrules. From the fluctuation data, we estimated the time-to-failure tf at which the ΔL value became 3 µm. We estimated the acceleration parameters, median lifetimes ξ, and hazard rates λ by using tf values based on Weibull statistics. The ξ values decreased rapidly with increasing temperature and relative humidity. We found we could expect small λ values of < 0.1 FIT (FIT=10-9/hour) and of 1 FIT for 20 years in a normal atmosphere (25C/50%RH) and in a more severe case of 25C/90%RH, respectively.
Shin SUMIDA Yasufumi YAMADA Mitsuho YASU Masao KAWACHI
The hybrid integration of light sources and a photodetector with high-silica channel waveguides on a silicon substrate was successfully demonstrated for optical transmitting-receiving module use. The loss characteristics were experimentally examined and its individual losses were investigated in detail based upon theoretical and experimental results.
Yoshito SHUTO Hirotsugu SATO Shuichi YANAGI Masayoshi OHNO Shin SUMIDA Shunichi TOHNO
We examined the creep properties and hazard rates of plastic split alignment sleeves to ensure the long-term reliablity of optical fiber connections. It required a gauge retention force Fr of more than 200 gf to suppress the fluctuation in the insertion loss of a plastic sleeve. From the fluctuation data, we estimated the time-to-failure tf at which the Fr value became 200 gf. We estimated the acceleration parameters, median lifetimes ξ, and hazard rates λ by using the tf values based on the Weibull statistics. The ξ values decreased rapidly with increasing temperature and relative humidity. Small λ values of < 0.01 FITs and of 1 FITs were expected for 20 years in a normal atmosphere (25C/50%RH) and in a more severe case of 25C/90%RH or 45C/50%RH.