The a-Si films deposited on quartz substrates were crystallized by lateral sweep annealing in steep temperature gradient using a gas burner. Random nucleation in amorphous region was effectively suppressed in the temperature gradient, so lateral solid phase epitaxial growth from crystallites generated at the initial stage of lateral sweep annealing spread over 100 µm. Their crystallographic orientations were mostly (100).