Masaru KURAMOTO A. Atsushi YAMAGUCHI Akira USUI Masashi MIZUTA
Continuous-wave operation at room-tempera-ture has been demonstrated for InGaN multi-quantum-well (MQW) laser diodes (LDs) grown on FIELO GaN substrates with a backside n-contact. This was made possible by introducing important new concept of reducing threading dislocations that occur during the growth of the GaN substrates. We found that InGaN active layers grown on FIELO GaN are superior to those grown on conventional sapphire substrates in terms of their growth mode and the resultant In compositional fluctuation. The fabricated laser diode shows the threshold current, the threshold current density and the threshold voltage were 36 mA, 5.4 kA/cm2 and 7.5 V, respectively, with the lasing wavelength of 412 nm and internal quantum efficiency as high as 98%.