Break operations of DC inductive (L=20mH) load currents up to about 5A with 14V were conducted in air with AgSnO2 contact pairs under different contact opening speeds, first up to 20mm/s and then to 200mm/s. Average break arc duration at each current level was calculated under the respective opening speeds. While break arc durations became shorter with increases in the opening speeds at larger current levels, such reduction tendencies were less significant with an increase of the contact opening speed from 20mm/s to 200mm/s, even when operated to break a load current of 5A. Both load current levels and contact opening speed levels seem to exhibit certain roles for realizing arc shortening effects.

In order to study the influences of contact opening speeds on arc extinction gap length characteristics, Ag contacts were operated to break DC inductive load currents from 0.1 A to 2.0 A at 14 V with contact opening speeds of 0.5 mm/s, 1 mm/s, 2 mm/s, 5 mm/s and 10 mm/s in a switching mechanism employing a stepping motor, and arc voltage waveforms were observed at each opening of the contacts. From the results, the average arc durations were determined at each current level under the respective contact opening speeds, and the average arc extinction gap lengths were calculated by multiplying the average arc duration value and the contact opening speed value. It was found that average arc durations showed no significant differences with increasing contact opening speeds. Thus, arc extinction gaps became larger at faster opening speeds in the inductive load conditions of this study.

The purpose of this study is to examine the impact of the opening speed on a breaking arc. The opening speeds are 10, 20 and 30 mm/s. The breaking arc is generated in a D.C. 42 V/10.5 A circuit, and the arc voltage, the arc current, the gap length and the arc spectrum intensity are measured. Arc temperature is calculated by using a Boltzmann plot. Even if the opening speed is changed, the arc temperature starts from a high temperature, and falls gradually to 4650-4750 K with time. Namely, the opening speed has no influence on the arc temperature.