Recently, reliable Pb (Ti, Zr) O3 (PZT) thin-film capacitors with robust switching endurance were fabricated successfully by incorporating oxidizable metal and oxide electrodes. However, the reasons for the drastic improvement in the switching endurance property was not clear. Degradation of polarizations by switching is called "polarization fatigue. " This paper describes the mechanisms of polarization fatigue, and discusses ways for improving of that property from the standpoints of microstructure, and of interactions between the PZT and the electrode materials of the capacitors. It is clearly identified that the causes of the fatigue are the unexpected formation of a surface transition layer of PZT, which is strongly dependent on the crystallization process, and a decrease in the interfacial capacitances due to the accumulation of oxygen vacancies between the PZT and non-oxidizable metal electrodes with high work functions such as Pt. Oxidizable metal and oxide electrodes suppress by oxidation-reduction reactions the accumulation of oxygen vacancies. Fatigue-free PZT thin-film capacitors can be formed if oxidizable metal or conductive oxide electrodes are incorporated in columnar-grain-structured PZT thin-film. In sharp contrast, fatigue and retention properties of PZT thin-film capacitors with Ir electrodes were degraded by modification of the PZT with 1 atm%-Nb and 1 atm%-La even though its grain structures were columnar.
The copyright of the original papers published on this site belongs to IEICE. Unauthorized use of the original or translated papers is prohibited. See IEICE Provisions on Copyright for details.
Copy
Katsuhiro AOKI, Yukio FUKUDA, Ken NUMATA, Akitoshi NISHIMURA, "Formation of Reliable Pb(Ti, Zr)O3 Thin-Film Capacitors for Read/Write Endurance of Ferroelectric Non-volatile Memories" in IEICE TRANSACTIONS on Electronics,
vol. E81-C, no. 4, pp. 537-544, April 1998, doi: .
Abstract: Recently, reliable Pb (Ti, Zr) O3 (PZT) thin-film capacitors with robust switching endurance were fabricated successfully by incorporating oxidizable metal and oxide electrodes. However, the reasons for the drastic improvement in the switching endurance property was not clear. Degradation of polarizations by switching is called "polarization fatigue. " This paper describes the mechanisms of polarization fatigue, and discusses ways for improving of that property from the standpoints of microstructure, and of interactions between the PZT and the electrode materials of the capacitors. It is clearly identified that the causes of the fatigue are the unexpected formation of a surface transition layer of PZT, which is strongly dependent on the crystallization process, and a decrease in the interfacial capacitances due to the accumulation of oxygen vacancies between the PZT and non-oxidizable metal electrodes with high work functions such as Pt. Oxidizable metal and oxide electrodes suppress by oxidation-reduction reactions the accumulation of oxygen vacancies. Fatigue-free PZT thin-film capacitors can be formed if oxidizable metal or conductive oxide electrodes are incorporated in columnar-grain-structured PZT thin-film. In sharp contrast, fatigue and retention properties of PZT thin-film capacitors with Ir electrodes were degraded by modification of the PZT with 1 atm%-Nb and 1 atm%-La even though its grain structures were columnar.
URL: https://global.ieice.org/en_transactions/electronics/10.1587/e81-c_4_537/_p
Copy
@ARTICLE{e81-c_4_537,
author={Katsuhiro AOKI, Yukio FUKUDA, Ken NUMATA, Akitoshi NISHIMURA, },
journal={IEICE TRANSACTIONS on Electronics},
title={Formation of Reliable Pb(Ti, Zr)O3 Thin-Film Capacitors for Read/Write Endurance of Ferroelectric Non-volatile Memories},
year={1998},
volume={E81-C},
number={4},
pages={537-544},
abstract={Recently, reliable Pb (Ti, Zr) O3 (PZT) thin-film capacitors with robust switching endurance were fabricated successfully by incorporating oxidizable metal and oxide electrodes. However, the reasons for the drastic improvement in the switching endurance property was not clear. Degradation of polarizations by switching is called "polarization fatigue. " This paper describes the mechanisms of polarization fatigue, and discusses ways for improving of that property from the standpoints of microstructure, and of interactions between the PZT and the electrode materials of the capacitors. It is clearly identified that the causes of the fatigue are the unexpected formation of a surface transition layer of PZT, which is strongly dependent on the crystallization process, and a decrease in the interfacial capacitances due to the accumulation of oxygen vacancies between the PZT and non-oxidizable metal electrodes with high work functions such as Pt. Oxidizable metal and oxide electrodes suppress by oxidation-reduction reactions the accumulation of oxygen vacancies. Fatigue-free PZT thin-film capacitors can be formed if oxidizable metal or conductive oxide electrodes are incorporated in columnar-grain-structured PZT thin-film. In sharp contrast, fatigue and retention properties of PZT thin-film capacitors with Ir electrodes were degraded by modification of the PZT with 1 atm%-Nb and 1 atm%-La even though its grain structures were columnar.},
keywords={},
doi={},
ISSN={},
month={April},}
Copy
TY - JOUR
TI - Formation of Reliable Pb(Ti, Zr)O3 Thin-Film Capacitors for Read/Write Endurance of Ferroelectric Non-volatile Memories
T2 - IEICE TRANSACTIONS on Electronics
SP - 537
EP - 544
AU - Katsuhiro AOKI
AU - Yukio FUKUDA
AU - Ken NUMATA
AU - Akitoshi NISHIMURA
PY - 1998
DO -
JO - IEICE TRANSACTIONS on Electronics
SN -
VL - E81-C
IS - 4
JA - IEICE TRANSACTIONS on Electronics
Y1 - April 1998
AB - Recently, reliable Pb (Ti, Zr) O3 (PZT) thin-film capacitors with robust switching endurance were fabricated successfully by incorporating oxidizable metal and oxide electrodes. However, the reasons for the drastic improvement in the switching endurance property was not clear. Degradation of polarizations by switching is called "polarization fatigue. " This paper describes the mechanisms of polarization fatigue, and discusses ways for improving of that property from the standpoints of microstructure, and of interactions between the PZT and the electrode materials of the capacitors. It is clearly identified that the causes of the fatigue are the unexpected formation of a surface transition layer of PZT, which is strongly dependent on the crystallization process, and a decrease in the interfacial capacitances due to the accumulation of oxygen vacancies between the PZT and non-oxidizable metal electrodes with high work functions such as Pt. Oxidizable metal and oxide electrodes suppress by oxidation-reduction reactions the accumulation of oxygen vacancies. Fatigue-free PZT thin-film capacitors can be formed if oxidizable metal or conductive oxide electrodes are incorporated in columnar-grain-structured PZT thin-film. In sharp contrast, fatigue and retention properties of PZT thin-film capacitors with Ir electrodes were degraded by modification of the PZT with 1 atm%-Nb and 1 atm%-La even though its grain structures were columnar.
ER -