1-3hit |
Min LIANG Jian CHEN Lin KANG Biaobing JIN Weiwei XU Peiheng WU
Low noise terahertz (THz) receivers based on superconducting niobium nitride (NbN) hot electron bolometer (HEB) mixers have been designed, fabricated and measured for applications in astronomy and cosmology. The NbN HEB mixer consists of a planar antenna and an NbN bridge connecting across the antenna's inner terminals on a high-resistivity Si substrate. To eliminate the influence of direct detection and instability of the local oscillation (LO) power, a wire grid has been used to change the input LO power for compensating the shift of bias current during Y-factor measurement. The double sideband (DSB) receiver noise temperatures at 4.2 K without corrections have been measured from 0.65 to 3.1 THz. The excess quantum noise factor β of about 4 has been obtained, which agrees well with the calculated value. Allan variance of the HEB has been characterized, and Allan time TA longer than 0.4 s is obtained. We also estimated the temperature resolution of the HEB from the Allan variance and obtained the minimum temperature resolution of 1.1 K using a Gunn oscillator with its multipliers at 0.65 THz as an LO source.
Huabing WANG Jian CHEN Kensuke NAKAJIMA Tsutomu YAMASHITA Peiheng WU
C-axis junction-arrays, with a-b plane sizes of sub-microns to 10 microns, were patterned on Bi2Sr2CaCu2O8+x single crystals with either a mesa or an overlap structure. We measured the current-voltage (I-V) characteristics with microwave irradiation at a few to 100 gigahertz. At a few gigahertz, often observed were chaotic properties. Under irradiation at 100 GHz, we successfully performed harmonic mixings between the 100 GHz signal and up to the 100th harmonic of a local oscillator at about 1 GHz. Given in this paper are discussions on the observation of individual Shapiro steps, and descriptions of the relevant results. Our experimental results show that intrinsic Josephson junctions in layered superconductors can be good candidates for high frequency applications.
Huabing WANG Jian CHEN Lixing YOU Peiheng WU Tsutomu YAMASHITA
In this paper, we review the progress in BiSrCaCuO-2212 Intrinsic Josephson junctions (IJJs) by summarizing our recent results in fabrication and high frequency experiments. Using a double-side fabrication process, a well defined number of intrinsic Josephson junctions in a well defined geometry can be fabricated. The junctions in the stack are quite homogeneous, and the power distribution of external irradiation among the junctions is even. Shapiro steps are clearly observed up to 2.5 THz, and the general condition for the occurrence of Shapiro steps at frequency frf is that it should be much greater than the plasma frequency fpl. Under certain conditions the Shapiro steps are zero-crossing, making some applications possible, such as quantum voltage standard etc.