This paper presents recent progress on high frequency and wide bandwidth GaN high power amplifiers (PAs) that are usable for high-data-rate wireless communications and modern radar systems. The key devices and design techniques for PA are described in this paper. The results of the state-of-the art GaN PAs for microwave to millimeter-wave applications and design methodology for ultra-wideband GaN PAs are shown. In order to realize high output power density, InAlGaN/GaN HEMTs were employed. An output power density of 14.8 W/mm in S-band was achieved which is 1.5 times higher than that of the conventional AlGaN/GaN HEMTs. This technique was applied to the millimeter-wave GaN PAs, and a measured power density at 96 GHz was 3 W/mm. The modified Angelov model was employed for a millimeter-wave design. W-band GaN MMIC achieved the maximum Pout of 1.15 W under CW operation. The PA with Lange coupler achieved 2.6 W at 94 GHz. The authors also developed a wideband PA. A power combiner with an impedance transformation function based on the transmission line transformer (TLT) technique was adopted for the wideband PA design. The fabricated PA exhibited an average Pout of 233 W, an average PAE of 42 %, in the frequency range of 0.5 GHz to 2.1 GHz.

Current collapse phenomenon is a well known obstacle in the AlGaN/GaN HEMTs. In order to improve the surface stability of HEMTs, we have investigated the SiN passivation film deposited by T-CVD, and we found that it improves both gate leakage current and current collapse phenomenon [1]. Moreover, we compared the T-CVD and PE-CVD passivation films, on high electric field DC and RF characteristics. We found that T-CVD SiN passivation film improves BVds-off by 30% because of the reduction of gate leakage current. It also improved ηd in the output power characteristics by load-pull measurement, which indicates the decrease of the current collapse phenomenon. Also we fabricated a multi-fingered 50 W-class AlGaN/GaN HEMT with T-CVD SiN passivation film and achieved 61.2% of high drain efficiency at frequency of 2.14 GHz, which was 3.6 points higher than that with PE-CVD SiN passivation film.

In AlGaN/GaN high electron mobility transistors (HEMTs), drain current reduction by current collapse phenomenon is a big obstacle for a high efficient operation of power amplifier application. In this study, we investigated the effects of SiN passivation film quality on the electrical characteristics of AlGaN/GaN HEMTs. First, we conducted some experiments to investigate the relationship between electrical characteristics of AlGaN/GaN HEMTs and various conditions of SiN passivation film by plasma enhanced chemical vapor deposition (PE-CVD). We found that both gate current leakage and current collapse were improved simultaneously by SiN passivation film deposited by optimized condition of NH3 and SiH4 gas flow. It is found that the critical parameter in the optimization is a IN-H/ ISi-H ratio measured by Fourier transforms infrared spectroscopy (FT-IR) spectra. Next, a thermal CVD SiN was applied to the passivation film to be investigated from the same point of view, because a thermal CVD SiN is well known to have good quality with low hydrogen content and high IN-H/ISi-H ratio. We confirmed that the thermal CVD SiN passivation could improve much further both of the gate leakage current and the current collapse in AlGaN/GaN-HEMTs. Furthermore, we tried to apply the thermal CVD SiN to the gate insulator in MIS (Metal Insulator Semiconductor) structure of AlGaN/GaN HEMTs. The thermal CVD SiN passivation was more suitable for the gate insulator than PE-CVD SiN passivation in a view of reducing current collapse phenomena. It could be believed that the thermal CVD SiN film is superior to the PE-CVD SiN film to achieve good passivation and gate insulator film for AlGaN/GaN HEMTs due to the low hydrogen content and the high IN-H/ISi-H ratio.

To reduce the gate leakage current of AlGaN/GaN HEMTs, we selected ITO/Ni/Au for Schottky electrodes and Schottky characteristics were compared with those of Ni/Au electrodes. ITO/Ni/Au and Ni/Au electrodes were deposited by vacuum evaporation and annealed at 350 in nitrogen atmosphere. From the I-V evaluation results of ITO/Ni/Au electrodes, forward and reverse leakage currents were reduced. Schottky characteristics of ITO/Ni/Au electrodes were also improved compared to these of Ni/Au electrodes. In addition, substantial decrease of leakage currents was confirmed after the annealing of HEMTs with ITO/Ni/Au electrodes. This may be explained that ITO/AlGaN interface state became lower by the annealing. By the temperature dependence of I-V curves, clear dependence was confirmed for the gates with ITO/Ni/Au electrodes. On the other hand, small dependence was observed for those with Ni/Au electrodes. From these results, tunnel leakage currents were dominant for the gates with Ni/Au electrode. Thermal emission current was dominant for the gates with ITO/Ni/Au electrode. The larger temperature dependence was caused that ITO/AlGaN interface states were smaller than those for Ni/Au electrode. It was suggested that suppressed AlGaN Schottky barrier thinning was caused by the surface defect donors, then tunneling leakage currents were decreased. We evaluated HEMT characteristics with ITO/Ni/Au electrode and Ni/Au electrode. Id max and Gm max were similar characteristics, but Vth with ITO/Ni/Au electrode was shifted +0.4 V than that with Ni/Au electrode due to the higher Schottky barrier. It was confirmed to have a good pinch-off currents and low gate leakage currents by ITO/Ni/Au electrodes.

The correlation between ohmic contact resistivity (ρc) and transconductance (gm) in AlGaN/GaN high-electron-mobility transistors (HEMTs) was investigated. To characterize ρc precisely, we fabricated a circular transmission line model (c-TLM) pattern adjoined to a field-effect transistor (FET) pattern on an HEMT. By measuring ohmic contact resistance and sheet resistance using the adjoined c-TLM, intrinsic transconductance (gm0), which is not influenced by the source resistance, can be estimated. The gm0 thus obtained is between 179 and 206 mS/mm. Then, it became possible to calculate the correlation between gm and (ρc. We found that ρc should be below 10-5 Ωcm2 for the improvement of gm in AlGaN/GaN HEMT when Rsh 400 Ω/.

DC and RF performances of AlGaN/GaN HEMTs are simulated using a two-dimensional device simulator with the material parameters of GaN and AlGaN. The cut-off frequency is estimated as 205 GHz at the gate length of 0.05 µm and the drain breakdown voltage at this gate length is over 10 V. The values are satisfactory for millimeter wavelength power applications. The use of thin AlGaN layers has key importance to alleviate gate parasitic capacitance effects at this gate length.

The first implementations of X-band AlGaN/GaN HEMT single-ended frequency doublers are presented in this paper. Two types of fundamental frequency signal reflector schemes have been demonstrated for the frequency doubler application. Open-circuited quarter-wavelength microstrip line at the fundamental frequency is utilized for the reflector in a conventional way. In the other architecture a printed antenna is employed as a radiator as well as a novel fundamental frequency reflector. A microstrip rectangular patch antenna operating at the second harmonic frequency of the doubler was designed and integrated with AlGaN/GaN HEMT based on active integrated antenna design concept. Using AlGaN/GaN HEMT with 1 mm gate periphery, two 4 to 8 GHz frequency doublers were designed by the described design methodologies, fabricated, and tested. For the conventional frequency doubler, a conversion gain of 0.6 dB and with an output power of 15 dBm was observed. A conversion gain of 5 dB and an output power of 25 dBm with embedded antenna gain were achieved at a drain voltage of 12 V for the doubler integrated with the patch antenna.